Au-Ni solid solutions studied by numerical relaxation

(Received 20 July 1992, accepted in revised form 16 November 1992)

Abstract
A semi-empirical potential based on the tight-binding second moment approximation is used to study Au-Ni solid solutions at 0 K. The energy of formation, the topological disorder, and the elastic constants are analysed within the whole concentration range. The results coincide very well with available experiments and may be explained by a frustration of the interatomic bondings by the fcc lattice. The size effect predominates over the chemical one and the analysis of interstitial sites shows that the local chemical surroundings lead to a splitting of the fcc lattice tetrahedral volumes.

Résumé
Un potentiel semi-empirique, issu de la méthode des liaisons fortes dans l'approximation du second moment, est utilisé pour étudier la solution solide Au-Ni à 0 K. L'énergie de formation, le désordre topologique et les constantes élastiques sont analysées pour toute l'étendue de concentration. Les résultats sont en très bon accord avec les données expérimentales disponibles et peuvent être interprétés par une frustration des liaisons atomiques par le réseau cfc. L'effet de taille est prépondérant devant l'effet chimique et l'analyse des sites interstitiels montre que l'environnement chimique local conduit à une levée de dégénérescence des volumes tétraédriques du réseau cfc.