Observation of monolayer Guinier-Preston zones in Al-at 1.7 % Cu
Bernard Jouffrey1 and Dominique Dorignac21 Ecole Centrale Paris, LMSS-Mat, Grande Voie des Vignes, 92295 Châtenay-Malabry, France
2 CEMES-LOE CNRS, B.P. 4347, 31055 Toulouse Cedex, France
(Received 21 February 1992, accepted in final form 6 April 1992)
Abstract
The formation of Guinier-Preston zones (GP zones), after quenching then followed by annealing (in this paper 20 hours at 130
C), explains the hardening of aluminum-copper light alloys, which is at the origin of their usefulness in metallurgy. In
this paper recent results in transmission electron microscopy (400 kV) are presented. Atomic resolution observations show
that many GP zones appear as monolayers (GP1). Contrast simulations show that the observed contrasts can be interpreted as
due to zones rich in copper. Ordering can be observed inside some of them.
Résumé
La présence de zones de Guinier-Preston (zone GP) aprés trempe et recuit (ici 20 heures à
C), explique le durcissement des alliages léger d'aluminium-cuivre, qui est à l'origine de leur intérêt pratique. Nous présentons
dans l'article qui suit, des observations menées en microscopie à haute résolution (400 kV), qui permettent d'affirmer que
les zones observées (GP1) sont des monocouches atomiques, plus riches en cuivre que la matrice. Une structure ordonnée peut
être observée à l'interieur de certaines zones.
© Les Editions de Physique 1992