Etude de films magnétiques de l'alliage Fe $\mathsf{_{60}}$Al $\mathsf{_{40}}$

A. Fnidiki and J. P. Eymery

Laboratoire de Métallurgie Physique U.R.A. 131 du C.N.R.S., 40, avenue du Recteur Pineau, F-86022 Poitiers Cedex, France


(Reçu le 10 décembre 1990, accepté sous forme définitive le 11 février 1991)

Abstract
We show that the coevaporation technique like ion implantation, allows us to obtain Fe 60Al 40 which is both chemically disordered and ferromagnetic at 293 K. However, differences between implanted bulk alloy and thin films of the same composition have been observed concerning the temperature evolution of magnetic properties. In the first case, magnetic effects disappear as soon as 400 K; in the second case, one still observes a significant ferromagnetic fraction at room temperature after annealing at 700 K and cooling down. Moreover, the hyperfine field at the 57 iron nucleus increases. This leads to the hypothesis of iron rich phases and hence indicates that the alloy does not reoder.

Résumé
On montre que la technique de coévaporation permet, comme l'implantation ionique, d'obtenir Fe 60Al 40 désordonné au point de vue atomique et ferromagnétique à 293 K. Il s'avère cependant qu'il y a des différences entre l'alliage massif implanté et les films minces de même composition en ce qui concerne l'évolution en température des propriétés magnétiques. Dans le premier cas, il y a disparition des effets magnétiques dès 400 K ; dans le second, on observe encore une fraction ferromagnétique importante après chauffage et retour à l'ambiante. De plus, le champ hyperfin au noyau du fer 57 croît, ce qui conduit à l'hypothèse de zones enrichies en fer et, par suite, indique que l'alliage ne se réordonne pas.