Caractérisation du dipôle lacune-calcium par relaxations électrique et mécanique dans des mononcristaux de zircones calciées

(Reçu Ie 9 novembre 1992, accepté le I8 janvier 1993)

Abstract
Complex impedance measurements have been performed on calcia doped zirconia single crystals for three different dopant concentrations. A maximum of the dielectric loss is observed at a frequency which is thermally activated. The activation energy is slightly lower than the one derived from the study of the dc electrical conductivity with temperature. The experimental results depend very little on composition. Resonant method experiments have been used to measure internal friction and Young's modulus for different orientations [100], [110] and [111] in he case of one composition. The study with temperature confirms that [111] is the preferential orientation of the vacancy-calcium dipole.

Résumé
Des mesures isothermes d'impédance complexe ont été réalisées sur des échantillons monocristallins de zircone cuhique stabilisée à la chaux, pour trois compositions différentes. L'étude de la conductivité en courant continu conduit à la détermination d'une énergie d'activation légèrement superieure à celle obtenue lors de l'étude en fréquence de l'angle de pertes diélectriques. Pour une concentration donnée, nous avons également mesuré, par une méthode de résonance, le frottement intérieur ainsi que le module d'Young d'un échantillon selon les trois orientations cristallographiques [100], [111] et [110]. Cette étude confirme la direction du dipôle lacune-calcium selon un axe [111].