Remarkable Influence of Heat Treatment on the Structural and Superconducting Properties of Y 1-xPr xSrBaCu 3O 6+z

A. Das and R. Suryanarayanan

Laboratoire de Physique des Solides de Bellevue, CNRS, 92195 Meudon, France

(Received 22 February 1995, revised 27 March 1995, accepted 19 April 1995)

Preparation, structural and superconducting properties of Y 1-xPr xSrBaCu 3O 6+z (YPSBCO) are reported. Preheating of the samples in argon prior to oxygen annealing not only increased the orthorhombic splitting but $T_{\rm c}$ also was enhanced by 5 to 14 K depending on x. Furthermore, this treatment induced superconductivity in the x=0.70 sample and $T_{\rm c}$ was found to be 14 K. The slope d $T_{\rm c}$/d x decreased considerably compared to Y 1-xPr xBa 2Cu 3O 6+z, where superconductivity was destroyed for $x\geq 0.55$. The data seem to indicate that a knowledge of the structural and defect chemistry is essential to understand the behaviour of Pr in YPSBCO.

© Les Editions de Physique 1995

Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.